Conveyor Belts
 Cotton canvas conveyor belt
 Nylon canvas conveyor belt
 Polyester Fabric Conveyor Belt
 EP conveyor belt
 Heat resistant conveyor belt
 Oil resistant conveyor belt
 Flame resistant conveyor belt
 Acid/alkali resistant conveyor belt
 High abrasion resistant conveyor belt
 Chevron pattern conveyor belt
 Corrugated sidewall conveyor belt
 Pipe conveyor belt
 Endless conveyor belt
 Foodstuff conveyor belt
 Rhombic Pattern conveyor belt
 Rough top conveyor belt
 Cold resistant conveyor belt
 High temperature conveyor belt
Industrial Rubber Sheet/ Mat
V-belts
Hot products
OEM rubber products
 
 
Conveyor Belts >> High temperature conveyor belt >> high temperature conveyor belt  



1. Specifications

Spec.

Fabric tensile strength N/mm

Top cover rubber thickness  mm

Bottom cover rubber thickness  mm

Fabric canvas plies

Width

mm

TG350

350

4.5-12

2-3

1

300-1600

TG450

450

4.5-12

2-3

1

300-1600

TG500

500

4.5-12

2-3

1

300-1600

TG600

600

4.5-12

2-3

1

300-1600

TG800

800

4.5-12

2-3

1

300-1600

TG1000

1000

4.5-12

2-3

1

300-1600

TG1250

1250

4.5-12

2-3

1

300-1600

Note

Special spec. can be done as customer’s requirement

 

Splice configurations : hot vulcanization , mechanical faste

 

2. Product Features :

   1. Envirnmental-friendly : take the latest technology imporved synthetic rubber as body material ,  adopt foreign advanced technology and first-class raw material . Key materials are all imported and in line with EU Environmental Standard ( no harmful gas when they are heated ) 

   2. New Design, Unique Structure : imported , high tensile strength , low thermal shrinkage fabric .The belt itself , high tensile strength , low extension .

1) solved the problem of blister and ply separation on the Multi-ply conveyor belts when they are heated

2) light weight, lighter than the same tensile strength conveyor belts ,  reduced the energy loss of conveying machinery , saved energy and improved economic benefit . 

 

3 Heat-resistant king conveyor belt ,high technology

   Adopt our own company technology standard, high better than International and domestic standard

ISO 4195 Standard

ITEM

TYPE

T1

T2

T3

T4

RANGE

Hardness

Difference before and after aging IRHD

+20

+20

+20

 

Maximum &#118alue after aging (IRHD)

85

85

85

 

Tensile Strength

Change rate of property  %

-25

-30

-40

 

Minimum &#118alue after aging  MPa

12

10

5

 

Breaking Elongation

Change rate of property after aging   %

-50

-50

-55

 

Minimum &#118alue after aging  %

200

200

180

 

GB/T 20021-2005 Standard

Hardness

Difference before and after aging IRHD

+20

+20

±20

±20

Maximum &#118alue after aging (IRHD)

85

85

85

85

Tensile Strength

Change rate of property  %

-25

-30

-40

-40

Minimum &#118alue after aging  MPa

12

10

5

5

Breaking Elongation

Change rate of property after aging %

-50

-50

-55

-55

Minimum &#118alue after aging   %

200

200

180

180

Company Standard

Hardness

Difference before and after aging IRHD

+10

+10

+10

+10

Maximum &#118alue after aging (IRHD)

70

70

70

70

Tensile Strength

Change rate of property  %

-15

-15

-15

-15

Minimum &#118alue after aging  MPa

14

12

10

10

Breaking Elongation

Change rate of property after aging %

-20

-20

-20

-20

Minimum &#118alue after aging   %

400

400

450

450

Note

T1Aging temperature 100°C , Aging time 168 hours

T2Aging temperature 125°C , Aging time 168 hours

T3Aging temperature 150°C , Aging time 168 hours

T4Aging temperature 175°C , Internatiol and domestic standard aging time 96 hours,company standard aging time 168 hours 

 

    Update Time:2014/7/11 【Print】 【Back  
 
 